API 5CT Cest on standard, mille on kehtestanud Ameerika naftainstituut (API) nafta ja maagaasi transportimiseks. See on õõnes, silindriline terasest toru, mis läbib erikohti, et suurendada selle vastupidavust ja töökindlust. Selle korpuse standardsuurused on vahemikus 4 tolli kuni 9 tolli, mis vastab erineva voolukiiruse vajadustele.
API 5CT COSING PORT andmetabel
| Sildida | Od mm |
Nominaalne Lineaarne Massb,c T&C kg/m |
Wt t mm |
Lõpu tüüp - viimistlusd | ||||||||
| H40 | J55 K55 |
M65 | L80 R95 |
N80 tüüp 1, Q |
C90 T95 |
P110 | Q125 | |||||
| 1 | 2 | |||||||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 |
| 4-1/2 4-1/2 4-1/2 4-1/2 4-1/2 |
9.50 10.50 11.60 13.50 15.10 |
114.30 114.30 114.30 114.30 114.30 |
14.14 15.63 17.26 20.09 22.47 |
5.21 5.69 6.35 7.37 8.56 |
PS - - - - |
PS PSB PSLB - - |
PS PSB PLB PLB - |
- - PLB PLB - |
- - PLB PLB - |
- - PLB PLB - |
- - PLB PLB PLB |
- - - - PLB |
| 5 5 5 5 5 5 5 |
11.50 13.00 15.00 18.00 21.40 23.20 24.10 |
127.00 127.00 127.00 127.00 127.00 127.00 127.00 |
17.11 19.35 22.32 26.79 31.85 34.53 35.86 |
5.59 6.43 7.52 9.19 11.10 12.14 12.70 |
- - - - - - - |
PS PSLB PSLBE - - - - |
PS PSLB PLB PLB PLB - - |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - - PLB PLB PLB PLB |
| 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 |
14.00 15.50 17.00 20.00 23.00 26.80 29.70 32.60 35.30 38.00 40.50 43.10 |
139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 |
20.83 23.07 25.30 29.76 34.23 39.88 44.20 48.51 52.53 56.55 60.27 61.14 |
6.20 6.98 7.72 9.17 10.54 12.70 14.27 15.88 17.45 19.05 20.62 22.22 |
PS - - - - - - - - - - - |
PS PSLBE PSLBE - - - - - - - - - |
PS PSLB PLB PLB PLB - - - - - - - |
- - Plbe Plbe Plbe - - - - - - - |
- - Plbe Plbe Plbe - - - - - - - |
- - Plbe Plbe Plbe P P P P P P P |
- - Plbe Plbe Plbe - - - - - - - |
- - - - Plbe - - - - - - - |
| 6-5/8 6-5/8 6-5/8 6-5/8 |
20.00 24.00 28.00 32.00 |
168.28 168.28 168.28 168.28 |
29.76 35.72 41.67 47.62 |
7.32 8.94 10.59 12.06 |
PS - - - |
PSLB PSLBE - - |
PSLB PLB PLB - |
- Plbe Plbe Plbe |
- Plbe Plbe Plbe |
- Plbe Plbe Plbe |
- Plbe Plbe Plbe |
- - - Plbe |
| 7 7 7 7 7 7 7 |
17.00 20.00 23.00 26.00 29.00 32.00 35.00 |
177.80 177.80 177.80 177.80 177.80 177.80 177.80 |
25.30 29.76 34.23 38.69 43.16 47.62 52.09 |
5.87 6.91 8.05 9.19 10.36 11.51 12.65 |
PS PS - - - - - |
- PS PSLBE PSLBE - - - |
- PS PLB PLB PLB PLB - |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - - PLB PLB PLB Plbe |
- - - - - - PLB |
| 7 7 7 7 7 7 |
38.00 42.70 46.40 50.10 53.60 57.10 |
177.80 177.80 177.80 177.80 177.80 177.80 |
56.55 63.54 69.05 74.56 79.77 84.97 |
13.72 15.88 17.45 19.05 20.62 22.22 |
- - - - - - |
- - - - - - |
- - - - - - |
PLB - - - - - |
PLB - - - - - |
PLB P P P P P |
PLB - - - - - |
PLB - - - - - |
| 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 |
24.00 26.40 29.70 33.70 39.00 42.80 45.30 47.10 51.20 55.30 |
193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 |
35.72 39.29 44.20 50.15 58.04 63.69 67.41 70.09 76.19 82.30 |
7.62 8.33 9.52 10.92 12.70 14.27 15.11 15.88 17.45 19.05 |
PS - - - - - - - - - |
- PSLB - - - - - - - - |
- PSLB PLB PLB - - - - - - |
- PLB PLB PLB PLB PLB PLB PLB - - |
- PLB PLB PLB PLB PLB PLB PLB - - |
- PLB PLB PLB PLB PLB PLB PLB P P |
- - PLB PLB PLB PLB PLB PLB - - |
- - - - PLB PLB PLB PLB - - |
| 7-3/4 | 46.10 | 196.85 | 68.60 | 15.11 | - | - | - | P | P | P | P | P |
| 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 |
24.00 28.00 32.00 36.00 40.00 44.00 49.00 |
219.08 219.08 219.08 219.08 219.08 219.08 219.08 |
35.72 41.67 47.62 53.57 59.53 65.48 72.92 |
6.71 7.72 8.94 10.16 11.43 12.70 14.15 |
- |
PS PS - PSLB PSLB PLB - |
PS PS PSLB PSLB PLB - - |
- - - PLB PLB PLB PLB |
- - - PLB PLB PLB Plbe |
- - - Plbe Plbe Plbe Plbe |
- - - PLB PLB PLB |
- - - - - PLB |
| 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 |
32.30 36.00 40.00 43.50 47.00 53.50 58.40 59.40 64.90 70.30 75.60 |
244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 |
48.07 53.57 59.53 64.73 69.94 79.62 86.91 88.40 96.58 104.62 112.50 |
7.92 8.94 10.03 11.05 11.99 13.84 15.11 15.47 17.07 18.64 20.24 |
PS PS - - - - - - - - - |
- PSLB PSLB - - - - - |
- PSLB PSLB PLB PLB - - - - - |
- - PLB PLB PLB PLB PLB - - - - |
- - PLB PLB PLB PLB PLB - - - |
- - PLB PLB PLB PLB PLB P P P P |
- - - PLB PLB PLB PLB - - - - |
- - - - PLB PLB PLB - - - - |
| 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 |
32.75 40.50 45.50 51.00 55.50 60.70 65.70 73.20 79.20 85.30 |
273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 |
48.74 60.27 67.71 75.90 82.59 90.33 97.77 108.93 117.86 126.94 |
7.09 8.89 10.16 11.43 12.57 13.84 15.11 17.07 18.64 20.24 |
PS PS - - - - - - - - |
- PSB PSB PSB - - - - - - |
- PSB PSB PSB PSB - - - - - |
- - - PSB PSB - - - - - |
- - - PSB PSB - - - - - |
- - - PSB PSB PSB PSB P P P |
- - - PSB PSB PSB PSB - - - |
- - - - - PSB PSB - - - |
| 11-3/4 11-3/4 11-3/4 11-3/4 11-3/4 11-3/4 |
42.00 47.00 54.00 60.00 65.00 71.00 |
298.45 298.45 298.45 298.45 298.45 298.45 |
62.50 69.94 80.36 89.29 96.73 105.66 |
8.46 9.53 11.05 12.42 13.56 14.78 |
PS - - - - - |
- PSB PSB PSB - - |
- PSB PSB PSB - - |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
| 13-3/8 13-3/8 13-3/8 13-3/8 13-3/8 |
48.00 54.50 61.00 68.00 72.00 |
339.72 339.72 339.72 339.72 339.72 |
71.43 81.10 90.78 101.19 107.15 |
8.38 9.65 10.92 12.19 13.06 |
PS - - - - |
- PSB PSB PSB - |
- PSB PSB PSB - |
- - - PSB PSB |
- - - PSB PSB |
- - - PSB PSB |
- - - PSB PSB |
- - - - PSB |
| 16 16 16 16 |
65.00 75.00 84.00 109.00 |
406.40 406.40 406.40 406.40 |
96.73 111.61 125.01 162.21 |
9.53 11.13 12.57 16.66 |
PS - - - |
- PSB PSB P |
- PSB PSB - |
- - - P |
- - - P |
- - - - |
- - - P |
- - - P |
| 18-5/8 | 87.50 | 473.08 | 130.21 | 11.05 | PS | PSB | PSB | - | - | - | - | - |
| 20 20 20 |
94.00 106.50 133.00 |
508.00 508.00 508.00 |
139.89 158.49 197.93 |
11.13 12.70 16.13 |
PSL - - |
PSLB PSLB PSLB |
PSLB PSLB - |
- - - |
- - - |
- - - |
- - - |
- - - |
| P=tavaline lõpp; S=lühikese ümmarguse lõime; L=pikk ümmargune niit; B--tuumaline niit; | ||||||||||||
|
V: Sildid on mõeldud teabe ja abi saamiseks tellimisel. B: nominaalsed lineaarsed massid (col . 4) on näidatud ainult teabe saamiseks. C: Martensiitsete kroomi teraste tihedused (L80 tüüpi 9CR ja 13CR) erinevad süsinikterastest. Seetõttu pole näidatud massid martensiitsete kroomi teraste puhul täpsed. Võib kasutada massiparandustegurit 0,989. D: Buttressi korpus on saadaval RegualR -i, spetsiaalsete lubade või spetsiaalsete kliirensiühendustega spetsiaalse kaldteega. |
||||||||||||
API 5ct korpuse materjalid Keemiline koostis
| Rühmitus | Aste | Tüüp | C | Mn | Mo | Cr |
Ni maksimaalne |
Cu maksimaalne |
P maksimaalne |
S maksimaalne |
Si maksimaalne |
||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| min | maksimaalne | min | maksimaalne | min | maksimaalne | min | maksimaalne | ||||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 | 15 | 16 |
|
1 |
H40 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
J55 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
K55 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
N80 |
1 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
N80 |
Q |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
R95 |
– |
– |
0.45 c |
– |
1.9 |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
0.45 |
|
|
2 |
M65 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
L80 |
1 |
– |
0.43 a |
– |
1.9 |
– |
– |
– |
– |
0.25 |
0.35 |
0.03 |
0.03 |
0.45 |
|
|
L80 |
9cr |
– |
0.15 |
0.3 |
0.6 |
0.9 |
1.1 |
8 |
10 |
0.5 |
0.25 |
0.02 |
0.01 |
1 |
|
|
L80 |
13cr |
0.15 |
0.22 |
0.25 |
1 |
– |
– |
12 |
14 |
0.5 |
0.25 |
0.02 |
0.01 |
1 |
|
|
C90 |
1 |
– |
0.35 |
– |
1.2 |
0.25 b |
0.85 |
– |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
|
T95 |
1 |
– |
0.35 |
– |
1.2 |
0.25 d |
0.85 |
0.4 |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
|
C110 |
– |
– |
0.35 |
– |
1.2 |
0.25 |
1 |
0.4 |
1.5 |
0.99 |
– |
0.02 |
0.005 |
– |
|
|
3 |
P110 |
e |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.030 e |
0.030 e |
– |
|
4 |
Q125 |
1 |
– |
0.35 |
1.35 |
– |
0.85 |
– |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
| a L80 süsinikusisaldus võib maksimaalselt suurendada, kui toode on õli - kustutatud. B Klassi C90 1. tüüpi molübdeenide sisaldusel pole minimaalset tolerantsi, kui seina paksus on alla 17,78 mm. C R95 süsinikusisaldust võib suurendada kuni 0,55 % -ni maksimaalselt, kui toode on õli - kustutatud. D T95 1. tüüpi molübdeenide sisaldust võib väheneda miinimumini 0,15 % -ni, kui seina paksus on väiksem kui 17,78 mm. E EW klassi P110 korral peab fosforisisaldus olema maksimaalselt 0,020 % ja väävli sisaldus 0,010 % maksimaalselt. Nl=pole piirangut. Näidatud elemendid tuleb esitada tooteanalüüsis. |
|||||||||||||||
Korpuse torumaterjalid - mehaanilised omadused
| Rühmitus |
Aste |
Tüüp |
Kogusumma pikenemine all koormus % |
Tootlus tugevus Mpa |
Tõmbe- tugevus min. Mpa |
Kõvadus a Max. |
Täpsustatud sein paksus mm |
Lubatav karedus variatsioon B Hrc |
||
|---|---|---|---|---|---|---|---|---|---|---|
| min | maksimaalne | Hrc | Hbw | |||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 |
| 1 |
H40 |
– |
0.5 |
276 |
552 |
414 |
– |
– |
– |
– |
|
J55 |
– |
0.5 |
379 |
552 |
517 |
– |
– |
– |
– |
|
|
K55 |
– |
0.5 |
379 |
552 |
655 |
– |
– |
– |
– |
|
|
N80 |
1 |
0.5 |
552 |
758 |
689 |
– |
– |
– |
– |
|
|
N80 |
Q |
0.5 |
552 |
758 |
689 |
– |
– |
– |
– |
|
|
R95 |
– |
0.5 |
655 |
758 |
724 |
– |
– |
– |
– |
|
| 2 |
M65 |
– |
0.5 |
448 |
586 |
586 |
22 |
235 |
– |
– |
|
L80 |
1 |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
L80 |
9cr |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
L80 |
13cr |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
C90 |
1 |
0.5 |
621 |
724 |
689 |
25.4 |
255 |
Vähem või võrdne 12,70 12.71 kuni 19.04 19.05 kuni 25,39 suurem kui 25,40 või võrdne |
3.0 4.0 5.0 6.0 |
|
|
T95 |
1 |
0.5 |
655 |
758 |
724 |
25.4 |
255 |
Vähem või võrdne 12,70 12.71 kuni 19.04 19.05 kuni 25,39 suurem või võrdne 25.40 |
3.0 4.0 5.0 6.0 |
|
|
C110 |
– |
0.7 |
758 |
828 |
793 |
30 |
286 |
Vähem või võrdne 12,70 12.71 kuni 19,0 19.05 kuni 25.39 Suurem kui 25,40 või võrdne |
3.0 4.0 5.0 6.0 |
|
| 3 |
P110 |
– |
0.6 |
758 |
965 |
862 |
– |
– |
– |
– |
| 4 |
Q125 |
1 |
0.65 |
862 |
1034 |
931 |
b |
– |
Vähem või võrdne 12,70 12,71 kuni 19,04 suurem või võrdne 19,05 |
3.0 4.0 5.0 |
| A Vaidluse korral tuleb kohtuniku meetodina kasutada laboratoorset Rockwell C kareduse testimist. b Kõvakuse piirid ei ole täpsustatud, kuid maksimaalne variatsioon on tootmiskontrolliks piiratud vastavalt API spec . 5 Ct 7,8 ja 7.9. |
||||||||||